MH196 Fast Curing, High-Temperature Gasketmaker, Red

In Stock

Permabond® MH196 is an anaerobic material that makes 'formed in situ' gaskets between metal surfaces. It can replace a wide range of conventional gaskets, thereby offering the potential for reduced stock holdings. By allowing surface-to-surface contact, load transmission can be improved. As the product does not shrink, creep, or relax after curing, no bolt retightening is required. It has excellent chemical and high-temperature resistance or up to 200°C.

Instant low pressure seal
Replaces all sizes of formed gaskets
Good high pressure resistance
High-temperature resistance
Does not creep or shrink

Tan bajo como USD 32.27

Saltar al final de la galería de imágenes

Saltar al comienzo de la galería de imágenes

Documentos técnicos

Product Info & TDS Sheets

Permabond MH196 Technical Data Sheet

Detalles

Más información
Código PAC	C100352
Marca	Permabond
Tipo	Fabricante de juntas

Más información

Physical Properties of Uncured Adhesive

Chemical composition: Acrylic
Appearance: Red
Viscosity @ 25°C:
- 2rpm: 500,000 mPa.s (cP)
- 20rpm: 100,000 mPa.s (cP)
Specific Gravity: 1.1
UV fluorescence: Yes

Typical Curing Properties

Maximum gap fill: 0.5mm (0.02")
Time taken to reach handling strength (M10 steel) @23°C: 15 minutes*
Time taken to reach working strength (M10 steel) @23°C: 1-3 hours
Full strength (M10 steel) @23°C: 24 hours

*Handling time at 23°C / 73°F. Copper and its alloys will make the adhesive cure more quickly, while oxidized or passivated surfaces (like stainless steel) will reduce cure speed. To reduce curing time, use Permabond activator A905 or ASC10 alternatively, increasing the curing temperature will reduce curing time.

Typical Performance of Cured Adhesive

Torque strength (M10 steel ISO10964)
- Break: 20 N·m (175 in.lb)
- Prevail: 23 N·m (200 in.lb)
Shear strength (steel collar & pin ISO10123): 10 MPa (1,450 psi)
Coefficient of thermal expansion: 90 x 10^-6mm/mm/°K
Dielectric strength: 11 kV/mm
Thermal conductivity: 0.19 W/(m.K)