ET5147 FDA Compliant High-Temperature Resistant Two-Part Epoxy, White/Ivory

In Stock

Permabond® ET5147 is a 2:1 mixable epoxy adhesive. It has excellent resistance to impact and vibration and is ideal for structural bonding of metal, wood, composites, and certain plastics. Its rapid cure speed coupled with its structural strength makes this adhesive suitable for a wide variety of applications. ET5147 is high strength and has excellent environmental durability. Permabond ET5147 has been specifically formulated to meet the requirements of FDA 175.105.

Adhesion to a wide variety of substrates
Full cure at room temperature
FDA Compliant formulation
High shear and peel strength
Good impact strength
Static mixer included with each cartridge

Tan bajo como USD 390.00

Saltar al final de la galería de imágenes

Saltar al comienzo de la galería de imágenes

Documentos técnicos

Product Info & TDS Sheets

Permabond ET5147 Technical Data Sheet

Detalles

Más información
Código PAC	C100400
Marca	Permabond
Tipo	Epoxi de dos partes

Más información

Physical Properties of Uncured Adhesive

	ET5147A	ET5147B
Chemical Composition	Epoxy Resin	Polyamine Hardener
Appearance	White	Ivory
Viscosity @25°C	20rpm: 25,000-40,000 mPa.s (cP) 2rpm: 80,000-160,000 mPa.s (cP)	20rpm: 90,000-150,000 mPa.s (cP) 2rpm: 150,000-300,000 mPa.s (cP)
Specific Gravity	1.3	1.2

Typical Curing Properties

Mix ratio by volume: 2:1
Maximum gap fill: 2mm (0.08")
Usable / pot life @23°C 2+1g: 40-60 mins
Handling time @23°C: 3-5 hours
Working strength:
- @23°C: 16 hours
- @60°C: 30 minutes
Full cure:
- @23°C: 72 hours
- @60°C: 1 hour

Typical Performance of Cured Adhesive

Shear strength* (ISO4587)
- Mild steel: 18-20 N/mm² (2600-2900 psi)
- Stainless steel: 15-19 N/mm² (2200-2800 psi)
- Aluminium: 10-14 N/mm² (1450 -2000 psi)
Peel strength (aluminum) (ISO4578): 40-70 N/25mm (9-16 PIW)
Hardness (ISO868): 68-72 Shore D
Glass transition temperature Tg: 50-60°C (122-140°F)
Dielectric strength: 15-25 kV/mm