Wescorp Anti-Static Conductive Shielding Grid Tape, 3" Core, 118' Rolls

• Low Charging Transparent Cellulose Film (2.4 Mil Thick) With High-Tack Rubber Adhesive - Wescorp tape generates less than 50 volts when unwound from roll (at 73°F, 45% RH average) making it safe to use around most ESD sensitive items.*
• Conductive Shielding Layer (1 x 10⁴ to < 1 x 10⁶ ohms) Marked with ESD Symbols (MIL STD 1285 and ESDA) - For use in creating a Faraday Cage to provide static shielding of an ESD sensitive item.
• Surface Resistance 1 x 10⁸ to < 1 x 10¹¹ohms - Tested per ANSI/ESD S11.11 to meet dissipative limits of packaging standard ANSI/ESD S541.
• Temperature Range 10°C - 71°C (14°F - 140°F) - Meets MIL-B-81705 for exposure to 100°C for 10 minutes max.
• Lead-Free RoHS Compliant
• Made in USA

Applications for Conductive Shielding Grid Tape

• For applications requiring EMI shielding
• Use in areas where the generation of static electricity is of concern
• Using grounded Tape Dispenser, voltage generated by unrolling will effectively be reduced to approaching zero
• Secure (bundle) IC tubes
• Cover external plugs, holes or connector pins on electronic chassis (black boxes, etc.) during transportation or storage

Specifications

Electrical Properties

• Both surfaces low-tribocharging at 50% RH
• Both surfaces low-tribocharging at 50% RH
• Conductive grid layer 1 x 10⁴ to < 1 x 10⁶ohms at 50% RH
• Adhesive copolymer resistivity 1 x 10⁹ohms (nominal) acrylic based adhesive
• Copolymer layer 8 x 10¹²ohms (nominal)

Physical Properties

• 1.9 Mil (0.0019"), (0.049mm) total thickness
• No silicone (adhesive, film backing, release material)
• Max Temperature 60°C (140°F)
• Non-corrosive

Property

• Tensile Strength - Longitudinal: 160 N/mm sq. ; Test Method: ASTM D 882
• Tensile Strength - Transverse: 270 N/mm sq.; Test Method: ASTM D 882
• Elongation - Longitudinal: 160%; Test Method: ASTM D 882
• Elongation - Transverse: 50%; Test Method: ASTM D 882
• Static Decay Time: 0.5 sec; Test Method: FTMS 101B, M4046
• Base Film Thickness: 30 micron
• Peeling Force: 12 N
• Cohesion Force: 12 hrs.; Test Method: LCTS-T2-4
• Adhesion to Steel: 0.300 kg/25mm min.; Test Method: LCTS-T3-4